3D4Makers ABS — ABS filament for FFF. Tensile strength 45 MPa · Density 1.05 g/cm³

3D4Makers ABS ESD — ABS filament for FFF. Tensile strength 24.3 MPa · Young's modulus 1121 MPa · Elongation at break 6.4 %

3D4Makers ABS Kevlar — ABS + Aramid (Kevlar) fibre filament for FFF. Tensile strength 35 MPa · Young's modulus 2350 MPa · HDT 75 °C

3D4Makers ASA — ASA filament for FFF. Tensile strength 47 MPa · Density 1.07 g/cm³

3D4Makers Facilan C8 — Filament for FFF. Tensile strength 45 MPa · Young's modulus 3000 MPa · HDT 55 °C

3D4Makers Facilan HT — Copolyester filament for FFF. Tensile strength 62 MPa · Young's modulus 2100 MPa · HDT 89 °C

3D4Makers Facilan Ortho — Polyester filament for FFF. Tensile strength 45 MPa · Young's modulus 350 MPa · HDT 57 °C

3D4Makers Facilan PCL 100 — PCL filament for FFF. Tensile strength 45 MPa · Young's modulus 350 MPa · HDT 57 °C

3D4Makers PEEK — PEEK filament for FFF. Tensile strength 105 MPa · Young's modulus 4100 MPa · Density 1.26 g/cm³

3D4Makers PEI Ultem 1000 — PEI filament for FFF. Tensile strength 105 MPa · Young's modulus 3200 MPa · Tg 217 °C

3D4Makers PEI Ultem 1010 — PEI filament for FFF. Tensile strength 105 MPa · Young's modulus 3200 MPa · Tg 217 °C

3D4Makers PEI Ultem 9085 — PEI filament for FFF. Tensile strength 84 MPa · Young's modulus 3440 MPa · Tg 186 °C

3D4Makers PEKK-A — PEKK filament for FFF. HDT 139 °C · Tg 158 °C · Density 1.27 g/cm³

3D4Makers PETG — PETG filament for FFF. Tensile strength 50 MPa · Young's modulus 2020 MPa · HDT 70 °C

3D4Makers PETG Carbon — PETG + Carbon Fiber filament for FFF. Tensile strength 52.9 MPa · Young's modulus 4015 MPa · Elongation at break 3.4 %

3D4Makers PI Z2 — PI filament for FFF. Tensile strength 83 MPa · Young's modulus 2730 MPa · Elongation at break 4.8 %

3D4Makers PLA — PLA filament for FFF. Tg 50 (approx.) °C · Density 1.24 (approx.) g/cm³

3D4Makers PLLA — PLLA filament for FFF. Tensile strength 50 MPa · Young's modulus 3500 MPa · Elongation at break ≤5 %

3D4Makers PPSU — PPSU filament for FFF. Density 1.29 g/cm³

3D4Makers R PEEK — PEEK filament for FFF. Tensile strength 90 MPa · Young's modulus 3400 MPa · Elongation at break 30 %

3D4Makers r-UltraMarathon PP GF — PP + Glass Fiber 30% filament for FFF. Tensile strength 67.1 MPa · Young's modulus 5463 MPa · Elongation at break 3.59 %

3DXTECH 3DXMAX ABS — ABS filament for FFF. Tensile strength 42 MPa · Young's modulus 1950 MPa · Elongation at break 10 %

3DXTECH 3DXMAX ASA — ASA filament for FFF. Tensile strength 45 MPa · Young's modulus 2010 MPa · Elongation at break 10 %

3DXTECH 3DXMAX HIPS — HIPS filament for FFF. Tensile strength 40 MPa · Young's modulus 1350 MPa · Elongation at break 18 %

3DXTECH 3DXMAX PC/ABS — PC/ABS filament for FFF. Tensile strength 59 MPa · Young's modulus 2200 MPa · Elongation at break 75 %

3DXTECH 3DXMAX PC/ASA — PC/ASA filament for FFF. Tensile strength 55 MPa · Young's modulus 2100 MPa · Elongation at break 35 %

3DXTECH 3DXMAX Polycarbonate — PC filament for FFF. Tensile strength 62 MPa · Young's modulus 2410 MPa · Elongation at break 7 %

3DXTECH 3DXPro Low-Gloss PETG — PETG filament for FFF. Tensile strength 47 MPa · Young's modulus 1400 MPa · Elongation at break 8 %

3DXTECH 3DXSTAT ESD-ABS — ABS filament for FFF. Tensile strength 58 MPa · Young's modulus 2130 MPa · Elongation at break 4 %

3DXTECH 3DXSTAT ESD-PC — PC filament for FFF. Tensile strength 68 MPa · Young's modulus 2300 MPa · Elongation at break 6 %

3DXTECH 3DXSTAT ESD-PEKK — PEKK filament for FFF. Tensile strength 109 MPa · Young's modulus 3300 MPa · Elongation at break 4 %

3DXTECH 3DXSTAT ESD-PETG — PETG filament for FFF. Tensile strength 50 MPa · Young's modulus 1800 MPa · Elongation at break 13 %

3DXTECH 3DXSTAT ESD-PLA — PLA filament for FFF. Tensile strength 55 MPa · Young's modulus 2560 MPa · Elongation at break 10 %

3DXTECH 3DXSTAT ESD-PPS — PPS filament for FFF. Tensile strength 55 MPa · Young's modulus 2600 MPa · Elongation at break 8 %

3DXTECH 3DXSTAT ESD-PVDF — PVDF filament for FFF. Tensile strength 55 MPa · Young's modulus 2635 MPa · Elongation at break 10 %

3DXTECH 3DXSTAT ESD-Safe Nylon 12 (PA12) — PA12 filament for FFF. Tensile strength 68 MPa · Young's modulus 6900 MPa · Elongation at break 3.8 %

3DXTECH 3DXSTAT ESD-TPU (90A) — TPU filament for FFF. Density 1.18 g/cm³

3DXTECH 3DXSTAT ESD-Ultem 1010 — PEI filament for FFF. Tensile strength 62 MPa · Young's modulus 2710 MPa · Elongation at break 4 %

3DXTECH AmideX PA6 Copolymer — PA6 filament for FFF. Tensile strength 55 MPa · Young's modulus 1980 MPa · Elongation at break 100 %

3DXTECH AmideX PA6-GF30 Glass Fiber Nylon — PA6 + Glass Fiber filament for FFF. Tensile strength 62.8 MPa · Young's modulus 4261 MPa · Elongation at break 6 %

3DXTECH CarbonX 20% Carbon Fiber PEEK — PEEK + Carbon Fiber 20% filament for FFF. Tensile strength 126 MPa · Young's modulus 10100 MPa · Elongation at break 1.9 %

3DXTECH CarbonX Carbon Fiber ABS — ABS + Carbon Fiber filament for FFF. Tensile strength 46 MPa · Young's modulus 5210 MPa · Elongation at break 2 %

3DXTECH CarbonX Carbon Fiber ASA — ASA + Carbon Fiber filament for FFF. Tensile strength 48 MPa · Young's modulus 5355 MPa · Elongation at break 3 %

3DXTECH CarbonX Carbon Fiber ezPC Polycarbonate — PC + Carbon Fiber filament for FFF. Tensile strength 73 MPa · Young's modulus 6980 MPa · Elongation at break 2.1 %

3DXTECH CarbonX Carbon Fiber High Temp Nylon (HTN) — HTN + Carbon Fiber filament for FFF. Tensile strength 87 MPa · Young's modulus 8200 MPa · Elongation at break 1.9 %

3DXTECH CarbonX Carbon Fiber Nylon (Gen3) — PA6 + Carbon Fiber filament for FFF. Tensile strength 63 MPa · Young's modulus 3800 MPa · Elongation at break 3 %

3DXTECH CarbonX Carbon Fiber Nylon 12 (PA12) — PA12 + Carbon Fiber filament for FFF. Tensile strength 72 MPa · Young's modulus 8000 MPa · Elongation at break 2.1 %

3DXTECH CarbonX Carbon Fiber PC/ABS — PC/ABS + Carbon Fiber filament for FFF. Tensile strength 62 MPa · Young's modulus 5900 MPa · Elongation at break 2 %

3DXTECH CarbonX Carbon Fiber PEEK — PEEK + Carbon Fiber filament for FFF. Tensile strength 105 MPa · Young's modulus 8100 MPa · Elongation at break 3 %

3DXTECH CarbonX Carbon Fiber PEKK-A CF15 [AERO] — PEKK + Carbon Fiber filament for FFF. Tensile strength 126 MPa · Young's modulus 9125 MPa · Elongation at break 3.15 %

3DXTECH CarbonX Carbon Fiber PETG — PETG + Carbon Fiber filament for FFF. Tensile strength 56 MPa · Young's modulus 5230 MPa · Elongation at break 3 %

3DXTECH CarbonX Carbon Fiber Polycarbonate — PC + Carbon Fiber filament for FFF. Tensile strength 70 MPa · Young's modulus 6200 MPa · Elongation at break 2 %

3DXTECH CarbonX Carbon Fiber Ultem 9085 — PEI + Carbon Fiber filament for FFF. Tensile strength 93 MPa · Young's modulus 8600 MPa · Elongation at break 2 %

3DXTECH CarbonX Carbon Fiber Ultem PEI — PEI + Carbon Fiber filament for FFF. Tensile strength 145 MPa · Young's modulus 7700 MPa · Elongation at break 1.5 %

3DXTECH CarbonX CF-PLA — PLA + Carbon Fiber filament for FFF. Tensile strength 48 MPa · Young's modulus 4950 MPa · Elongation at break 2 %

3DXTECH CarbonX PP+CF — PP + Carbon Fiber filament for FFF. Tensile strength 78 MPa · Young's modulus 6150 MPa · Elongation at break 1.5 %

3DXTECH ECOMAX PLA — PLA filament for FFF. Tensile strength 56 MPa · Young's modulus 2865 MPa · Elongation at break 8 %

3DXTECH ECOMAX Tough PLA — PLA filament for FFF. Tensile strength 53 MPa · Young's modulus 2272 MPa · Elongation at break 65 %

3DXTECH ezPC Polycarbonate — PC filament for FFF. Tensile strength 58 MPa · Young's modulus 2180 MPa · Elongation at break 14 %

3DXTECH FibreX ABS+GF10 Glass Fiber ABS — ABS + Glass Fiber 10% filament for FFF. Tensile strength 68 MPa · Young's modulus 4210 MPa · Elongation at break 2 %

3DXTECH FibreX PA12+GF30 — PA12 + Glass Fiber 30% filament for FFF. Tensile strength 82 MPa · Young's modulus 7800 MPa · Elongation at break 4.5 %

3DXTECH FibreX PP+GF30 — PP + Glass Fiber 30% filament for FFF. Tensile strength 65 MPa · Young's modulus 6750 MPa · Elongation at break 1.7 %

3DXTECH Firewire Flame Retardant ABS — ABS filament for FFF. Tensile strength 45 MPa · Young's modulus 1990 MPa · Elongation at break 4 %

3DXTECH Firewire Flame Retardant PC/ABS — PC/ABS filament for FFF. Tensile strength 60 MPa · Young's modulus 2250 MPa · Elongation at break 10 %

3DXTECH FluorX PVDF — PVDF filament for FFF. Tensile strength 51 MPa · Young's modulus 2450 MPa · Elongation at break 25 %

3DXTECH HyperLite PP — PP filament for FFF. Tensile strength 38 MPa · Young's modulus 1650 MPa · Elongation at break 13 %

3DXTECH MAX-G PCTG — PCTG filament for FFF. Tensile strength 45 MPa · Young's modulus 1755 MPa · Elongation at break 24 %

3DXTECH Obsidian Carbon Fiber Nylon — PA6 + Carbon Fiber filament for FFF. Tensile strength 44 MPa · Young's modulus 3500 MPa · Elongation at break 11 %

3DXTECH SimuBone Bone Simulation — Filament for FFF. Tensile strength 65 MPa · Young's modulus 3410 MPa · Elongation at break 4 %

3DXTECH ThermaX PEEK — PEEK filament for FFF. Tensile strength 100 MPa · Young's modulus 3720 MPa · Elongation at break 28 %

3DXTECH ThermaX PEEK GF20 — PEEK + Glass Fiber 20% filament for FFF. Tensile strength 105 MPa · Young's modulus 7250 MPa · Elongation at break 2.5 %

3DXTECH ThermaX PEI 1010 — PEI filament for FFF. Tensile strength 56 MPa · Young's modulus 2500 MPa · Elongation at break 3 %

3DXTECH ThermaX PEI 9085 — PEI filament for FFF. Tensile strength 54 MPa · Young's modulus 2050 MPa · Elongation at break 3 %

3DXTECH ThermaX PEI GF30 — PEI + Glass Fiber 30% filament for FFF. Tensile strength 145 (yield) MPa · Young's modulus 8790 MPa · Elongation at break 2 %

3DXTECH ThermaX PEKK-A — PEKK filament for FFF. Tensile strength 105 MPa · Young's modulus 2750 MPa · Elongation at break 5 %

3DXTECH ThermaX PEKK-C — PEKK filament for FFF. Tensile strength 105 MPa · Young's modulus 3200 MPa · Elongation at break 10 %

3DXTECH ThermaX PPE/PS — PPE/PS filament for FFF. Tensile strength 67 MPa · Young's modulus 2250 MPa · Elongation at break 12 %

3DXTECH ThermaX PPS — PPS filament for FFF. Tensile strength 50 MPa · Young's modulus 2650 MPa · Elongation at break 18 %

3DXTECH ThermaX PPSU — PPSU filament for FFF. Tensile strength 55 MPa · Young's modulus 2310 MPa · Elongation at break 3 %

3DXTECH ThermaX PSU — PSU filament for FFF. Tensile strength 52 MPa · Young's modulus 2100 MPa · Elongation at break 8 %

3DXTECH ThermaX TPI — TPI filament for FFF. Tensile strength 74 MPa · Young's modulus 2950 MPa · Elongation at break 6 %

3DXTECH WearX Wear Resistant PA6 Copolymer — PA6 filament for FFF. Tensile strength 62 MPa · Young's modulus 2458 MPa · Elongation at break 18 %

Dow EVOLV3D Olefin Block Copolymer (OBC) — OBC filament for FFF. Tensile strength 14 MPa · Elongation at break >700 % · Density 0.905 g/cm³

Fiberlogy ABS — ABS filament for FFF. Tensile strength 45 MPa · Young's modulus 2300 MPa · HDT 100 (annealed) °C

Fiberlogy ABS ESD — ABS filament for FFF. Tensile strength 55 MPa · Young's modulus 2100 MPa · Elongation at break 5 %

Fiberlogy ABS Plus — ABS filament for FFF. Tensile strength 45 MPa · Young's modulus 2300 MPa · HDT 100 (annealed) °C

Fiberlogy ABS+GF — ABS + Glass Fiber filament for FFF. Tensile strength 50 MPa · Young's modulus 3500 MPa · Elongation at break 3.5 %

Fiberlogy ASA — ASA filament for FFF. Tensile strength 43 MPa · Young's modulus 2500 MPa · Elongation at break 25 %

Fiberlogy ASA Matte — ASA filament for FFF. Tensile strength 43 MPa · Young's modulus 2300 MPa · Elongation at break 19 %

Fiberlogy BVOH — BVOH filament for FFF. Tensile strength 45 MPa · Elongation at break 9 % · Tg 68 °C

Fiberlogy CPE HT — CPE filament for FFF. Tensile strength 58 MPa · Young's modulus 1548 MPa · Elongation at break 185 %

Fiberlogy CPE HT+Ag Antibac — CPE filament for FFF. Tensile strength 58 MPa · Young's modulus 1548 MPa · Elongation at break 185 %

Fiberlogy Easy ABS — ABS filament for FFF. Tensile strength 44 MPa · Elongation at break 45 % · HDT 70 °C

Fiberlogy Easy PETG — PETG filament for FFF. Tensile strength 51 MPa · Young's modulus 2800 MPa · Elongation at break 29 %

Fiberlogy Easy PLA — PLA filament for FFF. Tensile strength 53 MPa · Young's modulus 3500 MPa · HDT 55 °C

Fiberlogy FiberFlex 30D — TPU filament for FFF. Tensile strength 22 MPa · Elongation at break 870 % · Density 1.07 g/cm³

Fiberlogy FiberFlex 40D — TPU filament for FFF. Tensile strength 28 MPa · Elongation at break 700 % · HDT 70 °C

Fiberlogy FiberFlex Aero — Filament for FFF. Tensile strength 28 (unfoamed) MPa · Elongation at break 700 (unfoamed) % · HDT 70 (unfoamed) °C

Fiberlogy FiberFlex+CF — TPU + Carbon Fiber filament for FFF. Tensile strength 60 MPa · Young's modulus 2200 MPa · Elongation at break 15 %

Fiberlogy HIPS — HIPS filament for FFF. Tensile strength 25 MPa · Young's modulus 1850 MPa · Elongation at break 31 %

Fiberlogy HS PLA Clear — PLA filament for FFF. Tensile strength 50 MPa · Young's modulus 3500 MPa · Elongation at break <5 %

Fiberlogy MattFlex 40D — Filament for FFF. Tensile strength 30 MPa · Elongation at break 600 % · HDT 70 °C

Fiberlogy Nylon PA12 — PA12 filament for FFF. Tensile strength 45 MPa · Young's modulus 1400 MPa · Elongation at break >50 %

Fiberlogy Nylon PA12+CF — PA12 + Carbon Fiber filament for FFF. Tensile strength 120 MPa · Young's modulus 7300 MPa · Elongation at break 5 %

Fiberlogy Nylon PA12+GF — PA12 + Glass Fiber filament for FFF. Tensile strength 72 MPa · Young's modulus 3100 MPa · Elongation at break 8 %

Fiberlogy PC ABS — PC/ABS filament for FFF. Tensile strength 42 MPa · Young's modulus 2000 MPa · Elongation at break 7 %

Fiberlogy PCTG — PCTG filament for FFF. Tensile strength 45 MPa · Elongation at break 220 % · HDT 64 °C

Fiberlogy PCTG+CF — PCTG + Carbon Fiber filament for FFF. Tensile strength 65 MPa · Elongation at break 5 % · HDT 64 °C

Fiberlogy PCTG+GF — PCTG + Glass Fiber filament for FFF. Tensile strength 25 MPa · Young's modulus 3400 MPa · Elongation at break 8 %

Fiberlogy PEI 9085 — PEI filament for FFF. Tensile strength 88 MPa · Young's modulus 3050 MPa · Elongation at break 70 %

Fiberlogy PETG ESD — PETG filament for FFF. Tensile strength 17.9 (3D printed) MPa · Young's modulus 2545 (3D printed) MPa · Elongation at break 8.0 (3D printed) %

Fiberlogy PETG FR V0 — PETG filament for FFF. Tensile strength 25 MPa · Young's modulus 2350 MPa · Elongation at break 40 %

Fiberlogy PETG Matte — PETG filament for FFF. Tensile strength 36.0 (3D printed) MPa · Young's modulus 2928 (3D printed) MPa · Elongation at break 4.6 (3D printed) %

Fiberlogy PETG+CF — PETG + Carbon Fiber filament for FFF. Tensile strength 105 MPa · Young's modulus 9000 MPa · Elongation at break 4 %

Fiberlogy PETG+PTFE — PETG filament for FFF. Tensile strength 25 MPa · Young's modulus 1850 MPa · Elongation at break >100 %

Fiberlogy PLA FiberSatin — PLA filament for FFF. Tensile strength 50 MPa · Young's modulus 2500 MPa · HDT 55 °C

Fiberlogy PLA FiberSilk — PLA filament for FFF. Tensile strength 42 MPa · Young's modulus 2300 MPa · HDT 55 °C

Fiberlogy PLA FiberWood — PLA filament for FFF. Tensile strength 26 MPa · Young's modulus 3600 MPa · Elongation at break 0.9 %

Fiberlogy PLA Impact — PLA filament for FFF. Tensile strength 40 MPa · Young's modulus 2870 MPa · HDT 75 – 85 °C

Fiberlogy PLA Matte — PLA filament for FFF. Tensile strength 41 MPa · HDT 55 °C · Tg 55 - 60 °C

Fiberlogy PLA Mineral — PLA filament for FFF. Tensile strength 30 MPa · Young's modulus 3500 MPa · Elongation at break 23 %

Fiberlogy PLA+CF — PLA + Carbon Fiber filament for FFF. Tensile strength 50 MPa · Young's modulus 8500 MPa · Elongation at break 2.4 %

Fiberlogy PP — PP filament for FFF. Tensile strength 14 MPa · Young's modulus 700 MPa · Elongation at break >100 %

Fiberlogy PVB FiberSmooth — PVB filament for FFF. Tensile strength 51 MPa · Young's modulus 3050 MPa · Elongation at break 88 %

Fiberlogy rABS — ABS filament for FFF. Tensile strength 45 MPa · Young's modulus 2300 MPa · HDT 100 (annealed) °C

Fiberlogy rNylon — PA12 filament for FFF. Tensile strength 45 MPa · Young's modulus 1400 MPa · Elongation at break >50 %

Fiberlogy rPETG — PETG filament for FFF. Tensile strength 51 MPa · Young's modulus 2800 MPa · Elongation at break 29 %

Fiberlogy rPLA — PLA filament for FFF. Tensile strength 53 MPa · Young's modulus 3500 MPa · HDT 55 °C

Fiberlogy rPP — PP filament for FFF. Tensile strength 14 MPa · Young's modulus 700 MPa · Elongation at break >100 %

Fiberon ASA-CF08 — ASA + Carbon Fiber filament for FFF. Tensile strength 43.5 ± 0.7 MPa · Young's modulus 3611.7 ± 181.1 MPa · Elongation at break 1.8 ± 0.1 %

Fiberon PA12-CF10 — PA12 + Carbon Fiber filament for FFF. Tensile strength 77.4 ± 1.1 MPa · Young's modulus 3311.2 ± 134.9 MPa · Elongation at break 4.2 ± 0.4 %

Fiberon PA6-CF20 — PA6 + Carbon Fiber filament for FFF. Tensile strength 109.3 ± 2.4 MPa · Young's modulus 8636.5 ± 211.4 MPa · Elongation at break 2.1 ± 0.2 %

Fiberon PA6-GF25 — PA6 + Glass Fiber filament for FFF. Tensile strength 80.1 ± 1.8 MPa · Young's modulus 5356.9 ± 211.0 MPa · Elongation at break 2.4 ± 0.2 %

Fiberon PA612-CF15 — PA612 + Carbon Fiber filament for FFF. Tensile strength 91.9 ± 2.0 MPa · Young's modulus 5136.7 ± 192.2 MPa · Elongation at break 2.6 ± 0.2 %

Fiberon PA612-ESD — PA612 filament for FFF. Tensile strength 84.3 ± 2.3 MPa · Young's modulus 4293.7 ± 116.4 MPa · Elongation at break 3.0 ± 0.1 %

Fiberon PET-CF17 — PET + Carbon Fiber filament for FFF. Tensile strength 65.9 ± 1.0 MPa · Young's modulus 5481.0 ± 223.7 MPa · Elongation at break 2.4 ± 0.5 %

Fiberon PETG-ESD — PETG filament for FFF. Tensile strength 36.1 ± 0.9 MPa · Young's modulus 1983.0 ± 74.9 MPa · Elongation at break 7.3 ± 0.7 %

Fiberon PETG-rCF08 — PETG + Carbon Fiber filament for FFF. Tensile strength 59.8 ± 0.3 MPa · Young's modulus 3710.1 ± 151.1 MPa · Elongation at break 5.7 ± 1.0 %

Fiberon PPS-CF10 — PPS + Carbon Fiber filament for FFF. Tensile strength 59.4 ± 1.3 MPa · Young's modulus 5446.7 ± 149.0 MPa · Elongation at break 1.4 ± 0.1 %

Fiberon PPS-GF20 — PPS + Glass Fiber filament for FFF. Tensile strength 64.1 ± 2.1 MPa · Young's modulus 4552.0 ± 54.6 MPa · Elongation at break 2.0 ± 0.2 %

Formfutura Bulk PETG Pellets — PETG pellets for Pellet extrusion. Tensile strength 29 MPa · Elongation at break 168 % · Density 1.28 g/cm³

Formfutura Castable LCD Resin Castable Wax — Photopolymer resin for LCD/MSLA

Formfutura Centaur PP Medical Grade Pellets — PP pellets for Pellet extrusion. Tensile strength 26.2 MPa · Elongation at break 642 % · Density 0.9 g/cm³

Formfutura Centaur PP Pellets — PP pellets for Pellet extrusion. Tensile strength 26.2 MPa · Elongation at break 642 % · Density 0.9 g/cm³

Formfutura Dental LCD Resin Model — Photopolymer resin for LCD/MSLA. Tensile strength 46 MPa · Young's modulus 1100 MPa · Elongation at break 8 %

Formfutura EasyFil ePLA Pellets — PLA pellets for Pellet extrusion. Tensile strength 46 MPa · Young's modulus 3530 MPa · Elongation at break 4.9 %

Formfutura Engineering LCD Resin Flex 63A — Photopolymer resin for LCD/MSLA. Tensile strength 1.7 MPa · Elongation at break 50–80 % · Density 1.18 g/cm³

Formfutura Engineering LCD Resin Flex 82A — Photopolymer resin for LCD/MSLA. Tensile strength 12 MPa · Young's modulus 80 MPa · Elongation at break 35 %

Formfutura Engineering LCD Resin Impact 71D — Photopolymer resin for LCD/MSLA. Tensile strength 41.5 MPa · Young's modulus 1300 MPa · Elongation at break 19 %

Formfutura Engineering LCD Resin Strong — Photopolymer resin for LCD/MSLA. Tensile strength 72 MPa · Young's modulus 1500–2500 MPa · Elongation at break 6 %

Formfutura Engineering LCD Resin Ultimate 2TW — Photopolymer resin for LCD/MSLA. Tensile strength 51 MPa · Young's modulus 1700 MPa · Elongation at break 90 %

Formfutura Engineering SLA Resin Heavy Duty — Photopolymer resin for SLA. Tensile strength 91 MPa · Young's modulus 2500 MPa · Elongation at break 8 %

Formfutura Engineering SLA Resin Tough — Photopolymer resin for SLA. Tensile strength 45 MPa · Young's modulus 1400 MPa · Elongation at break 25 %

Formfutura High Performance Resin Rigid Ceramic — Photopolymer + Ceramic-filled resin for LCD/MSLA. Tensile strength 70–85 MPa · Young's modulus 8500–9500 MPa · Elongation at break 1 %

Formfutura Miniature LCD Resin Model — Photopolymer resin for LCD/MSLA. Tensile strength 36.1 MPa · Young's modulus 1360 MPa · Elongation at break 6 %

Formfutura PEI ULTEM 9085 — PEI filament for FFF. Tensile strength 74 MPa · Young's modulus 3440 MPa · Elongation at break 72 %

Formfutura Platinum LCD Resin General Purpose — Photopolymer resin for LCD/MSLA. Tensile strength 45 MPa · Young's modulus 1000 MPa · Elongation at break 8 %

Formfutura PPSU — PPSU filament for FFF. Tensile strength 69.6 MPa · Young's modulus 2340 MPa · Elongation at break 60 to 120 %

Formfutura ReForm rPETG Frosted Pellets — PETG pellets for Pellet extrusion. Young's modulus 2220 MPa · Elongation at break 37 % · HDT 64 °C

Formfutura ReForm rPETG Frosted UV Pellets — PETG pellets for Pellet extrusion. Young's modulus 2220 MPa · Elongation at break 37 % · HDT 64 °C

Formfutura ReForm rPETG GB10 Pellets — PETG + Glass beads 10% pellets for Pellet extrusion. Tensile strength 50 MPa · Young's modulus 2530 MPa · Elongation at break 10 %

Formfutura ReForm rPETG GB10 UV Pellets — PETG + Glass beads 10% pellets for Pellet extrusion. Tensile strength 50 MPa · Young's modulus 2530 MPa · Elongation at break 10 %

Formfutura ReForm rPETG GF10 Pellets — PETG + Glass Fiber 10% pellets for Pellet extrusion. Tensile strength 70 MPa · Young's modulus 4200 MPa · Elongation at break 4 %

Formfutura ReForm rPETG GF10 UV Pellets — PETG + Glass Fiber 10% pellets for Pellet extrusion. Tensile strength 70 MPa · Young's modulus 4200 MPa · Elongation at break 4 %

Formfutura ReForm rPETG GF20 Pellets — PETG + Glass Fiber 20% pellets for Pellet extrusion. Tensile strength 75 MPa · Young's modulus 4500 MPa · Elongation at break 4 %

Formfutura ReForm rPETG GF20 UV Pellets — PETG + Glass Fiber 20% pellets for Pellet extrusion. Tensile strength 75 MPa · Young's modulus 4500 MPa · Elongation at break 4 %

Formfutura ReForm rPETG GF30 UV Pellets — PETG + Glass Fiber 30% pellets for Pellet extrusion. Tensile strength 100 MPa · Young's modulus 8000 MPa · Elongation at break 2.2 %

Formfutura ReForm rPETG Transparent FR for Building Applications EU Pellets — PETG pellets for Pellet extrusion. Young's modulus 2244 MPa · Elongation at break 37 % · HDT 64 °C

Formfutura ReForm rPETG Transparent Pellets — PETG pellets for Pellet extrusion. Tensile strength 28.6 MPa · Elongation at break 165 % · HDT 77 °C

Formfutura ReForm rPLA Matt UV Pellets — PLA + Mineral-filled pellets for Pellet extrusion. Tensile strength 32 MPa · Young's modulus 1850 MPa · HDT ~60 °C

Formfutura ReForm rPLA Pellets — PLA pellets for Pellet extrusion. Tensile strength 42 MPa · Young's modulus 3350 MPa · Elongation at break 4.7 %

Formfutura ReForm rPP GF10 UV Pellets — PP + Glass Fiber 10% pellets for Pellet extrusion. Tensile strength 30 MPa · Young's modulus 2100 MPa · Elongation at break 6.5 %

Formfutura ReForm rPP GF30 UV Pellets — PP + Glass Fiber 30% pellets for Pellet extrusion. Tensile strength 45 MPa · Young's modulus 4500 MPa · Elongation at break 6 %

Formfutura ReForm rPP Wood UV Pellets — PP + Wood fill pellets for Pellet extrusion. Tensile strength 19 MPa · Young's modulus 2000 MPa · Elongation at break 9 %

Formlabs Alumina 4N Resin — Alumina resin for SLA

Formlabs BioMed Amber Resin — Photopolymer resin for SLA. Tensile strength 73 MPa · Young's modulus 2900 MPa · Elongation at break 12 %

Formlabs BioMed Black Resin — Photopolymer resin for SLA. Tensile strength 36 MPa · Young's modulus 1500 MPa · Elongation at break 14 %

Formlabs BioMed Clear Resin — Photopolymer resin for SLA. Tensile strength 52 MPa · Young's modulus 2080 MPa · Elongation at break 12 %

Formlabs BioMed Durable Resin — Photopolymer resin for SLA. Tensile strength 29.1 MPa · Young's modulus 994 MPa · Elongation at break 33 %

Formlabs BioMed Flex 50A Resin — Photopolymer resin for SLA. Tensile strength 2.3 MPa · Elongation at break 150 % · Tg -36 °C

Formlabs BioMed Flex 80A Resin — Photopolymer resin for SLA. Tensile strength 7.2 MPa · Elongation at break 135 % · Tg 37 °C

Formlabs BioMed White Resin — Photopolymer resin for SLA. Tensile strength 46 MPa · Young's modulus 2000 MPa · Elongation at break 10 %

Formlabs Black Resin V5 — Photopolymer resin for SLA. Tensile strength 57 MPa · Young's modulus 2450 MPa · Elongation at break 14 %

Formlabs Castable Wax Resin — Photopolymer resin for SLA. Tensile strength 12 MPa · Young's modulus 220 MPa · Elongation at break 13 %

Formlabs Ceramic Resin — Photopolymer resin for SLA. Young's modulus 5100 MPa · HDT 75 °C

Formlabs Clear Cast Resin — Photopolymer resin for SLA. Tensile strength 65 MPa · Young's modulus 2800 MPa · Elongation at break 6 %

Formlabs Clear Resin V5 — Photopolymer resin for SLA. Tensile strength 51 MPa · Young's modulus 2575 MPa · Elongation at break 10 %

Formlabs Color Resin V5 — Photopolymer resin for SLA. Tensile strength 54 MPa · Young's modulus 2500 MPa · Elongation at break 15 %

Formlabs Custom Tray Resin — Photopolymer resin for SLA. Tensile strength >70 MPa · Young's modulus >2500 MPa · Elongation at break >3 %

Formlabs Dental LT Clear Resin V2 — Photopolymer resin for SLA. Tensile strength 52 MPa · Young's modulus 2080 MPa · Elongation at break 12 %

Formlabs Dental LT Comfort Resin — Photopolymer resin for SLA. Elongation at break 33 %

Formlabs Denture Base Resin V2 — Photopolymer resin for SLA. Tensile strength 57 MPa · Young's modulus 2800 MPa · Density 1.15 g/cm³

Formlabs Draft Resin — Photopolymer resin for SLA. Tensile strength 36 MPa · Young's modulus 1700 MPa · Elongation at break 5 %

Formlabs Durable Resin — Photopolymer resin for SLA. Tensile strength 28 MPa · Young's modulus 1000 MPa · Elongation at break 55 %

Formlabs ESD Resin — Photopolymer resin for SLA. Tensile strength 44.2 MPa · Young's modulus 1937 MPa · Elongation at break 12 %

Formlabs Fast Model Resin — Photopolymer resin for SLA. Tensile strength 55 MPa · Young's modulus 2480 MPa · Elongation at break 15 %

Formlabs Flame Retardant Resin — Photopolymer resin for SLA. Tensile strength 38 MPa · Young's modulus 2900 MPa · Elongation at break 9.4 %

Formlabs Flexible 50A Resin — Photopolymer resin for SLA. Tensile strength 3.4 MPa · Elongation at break 160 % · Tg -34.5 °C

Formlabs Flexible 80A Resin V2 — Photopolymer resin for SLA. Tensile strength 10.0 MPa · Elongation at break 230 % · Tg -49 °C

Formlabs Grey Pro Resin — Photopolymer resin for SLA. Tensile strength 61 MPa · Young's modulus 2600 MPa · Elongation at break 13 %

Formlabs Grey Resin V5 — Photopolymer resin for SLA. Tensile strength 54 MPa · Young's modulus 2500 MPa · Elongation at break 15 %

Formlabs High Temp Resin — Photopolymer resin for SLA. Tensile strength 58 MPa · Young's modulus 2800 MPa · Elongation at break 3.3 %

Formlabs IBT Flex Resin — Photopolymer resin for SLA. Tensile strength 7.2 MPa · Young's modulus 8 MPa · Elongation at break 135 %

Formlabs Model Resin — Photopolymer resin for SLA. Tensile strength 48 MPa · Young's modulus 2300 MPa · Elongation at break 4.8 %

Formlabs Nylon 11 CF Powder — PA11 + Carbon Fiber powder for SLS. Tensile strength 69 MPa · Young's modulus 5300 MPa · Elongation at break 9 %

Formlabs Nylon 11 Powder — PA11 powder for SLS. Tensile strength 49 MPa · Young's modulus 1600 MPa · Elongation at break 40 %

Formlabs Nylon 12 GF Powder — PA12 powder for SLS. Tensile strength 38 MPa · Young's modulus 2800 MPa · Elongation at break 4 %

Formlabs Nylon 12 Powder — PA12 powder for SLS. Tensile strength 50 MPa · Young's modulus 1850 MPa · Elongation at break 11 %

Formlabs Nylon 12 Tough Powder — PA12 powder for SLS. Tensile strength 42 MPa · Young's modulus 1450 MPa · Elongation at break 25 %

Formlabs Nylon 12 White Powder — PA12 powder for SLS. Tensile strength 47 MPa · Young's modulus 1950 MPa · Elongation at break 8 %

Formlabs Permanent Crown Resin — Photopolymer resin for SLA

Formlabs Polypropylene Powder — PP powder for SLS. Tensile strength 29 MPa · Young's modulus 1640 MPa · Elongation at break 34 %

Formlabs Precision Model Resin — Photopolymer resin for SLA. Tensile strength 50 MPa · Young's modulus 2200 MPa · Elongation at break 8.60 %

Formlabs Premium Teeth Resin — Photopolymer resin for SLA

Formlabs PU Rigid 1000 Resin — Polyurethane resin for SLA. Tensile strength 35 ± 3.5 MPa · Young's modulus 920 ± 90 MPa · Elongation at break 80 ± 8 %

Formlabs PU Rigid 650 Resin — Polyurethane resin for SLA. Tensile strength 34 ± 3.4 MPa · Young's modulus 670 ± 60 MPa · Elongation at break 170 ± 17 %

Formlabs Rigid 10K Resin — Photopolymer + Glass-filled resin for SLA. Tensile strength 65 MPa · Young's modulus 10000 MPa · Elongation at break 1 %

Formlabs Rigid 4000 Resin — Photopolymer + Glass-filled resin for SLA. Tensile strength 69 MPa · Young's modulus 4100 MPa · Elongation at break 5.3 %

Formlabs Silicone 40A Resin — Silicone resin for SLA. Tensile strength 5 MPa · Elongation at break 230 % · Tg -107 °C

Formlabs Surgical Guide Resin — Photopolymer resin for SLA. Elongation at break 12 %

Formlabs Tough 1000 Resin — Photopolymer resin for SLA. Tensile strength 26.3 MPa · Young's modulus 932 MPa · Elongation at break 180 %

Formlabs Tough 1500 Resin V2 — Photopolymer resin for SLA. Tensile strength 34 MPa · Young's modulus 1460 MPa · Elongation at break 155 %

Formlabs Tough 2000 Resin V2 — Photopolymer resin for SLA. Tensile strength 40.4 MPa · Young's modulus 1800 MPa · Elongation at break 79 %

Formlabs TPU 90A Powder — TPU powder for SLS. Tensile strength 8.7 MPa · Elongation at break 310 % · Density 1.14 g/cm³

Formlabs White Resin V5 — Photopolymer resin for SLA. Tensile strength 54 MPa · Young's modulus 2500 MPa · Elongation at break 15 %

HP 3D HR PA 11 — PA11 powder for MJF. Tensile strength 54 MPa · Young's modulus 1700 MPa · Elongation at break 40 %

HP 3D HR PA 11 Gen2 — PA11 powder for MJF. Tensile strength 52 MPa · Young's modulus 1740 MPa · Elongation at break 35 %

HP 3D HR PA 12 FR — PA12 powder for MJF. Tensile strength 46 MPa · Young's modulus 2580 MPa · Elongation at break 4.7 %

HP 3D HR PA 12 Glass Beads — PA12 + Glass Beads 40% powder for MJF. Tensile strength 31 MPa · Young's modulus 2900 MPa · Elongation at break 9 %

HP 3D HR PA 12 S — PA12 powder for MJF. Tensile strength 45 MPa · Young's modulus 1700 MPa · Elongation at break 12 %

HP 3D HR PP — PP powder for MJF. Tensile strength 29 MPa · Young's modulus 1600 MPa · Elongation at break 16 %

HP 3D HR TPU 01 — TPU powder for MJF. Tensile strength 9 MPa · Elongation at break 291 % · Density 1.11 g/cm³

Kexcelled MOLEGRID ABS-Like — Photopolymer resin for LCD/MSLA. Tensile strength 42 MPa · Elongation at break 18.2 %

Kexcelled MOLEGRID ABS+ — Photopolymer resin for LCD/MSLA. Tensile strength 43 MPa · Elongation at break 24.2 %

Kexcelled MOLEGRID AcryFlex — Photopolymer resin for LCD/MSLA. Tensile strength 9.20 MPa · Elongation at break 359 %

Kexcelled MOLEGRID AcryHD — Photopolymer resin for LCD/MSLA. Tensile strength 40 MPa · Elongation at break 13 %

Kexcelled MOLEGRID AcryHeat — Photopolymer resin for LCD/MSLA. Tensile strength 52 MPa · HDT >250 °C

Kexcelled MOLEGRID AcryPix — Photopolymer resin for LCD/MSLA. Tensile strength 52.32 MPa · Elongation at break 7.03 % · HDT 95 °C

Kexcelled MOLEGRID Basic — Photopolymer resin for LCD/MSLA. Tensile strength 61 MPa · Elongation at break 11.4 %

Kexcelled MOLEGRID Bio-based — Photopolymer resin for LCD/MSLA. Tensile strength 35.94 MPa · Elongation at break 12.17 %

Kexcelled MOLEGRID Clear — Photopolymer resin for LCD/MSLA. Tensile strength 34.32 MPa

Kexcelled MOLEGRID Denture — Photopolymer resin for LCD/MSLA

Kexcelled MOLEGRID Fast — Photopolymer resin for LCD/MSLA. Tensile strength 32 MPa · Elongation at break 10.5 %

Kexcelled MOLEGRID Flexible — Photopolymer resin for LCD/MSLA. Tensile strength 9.2 MPa · Elongation at break 359 %

Kexcelled MOLEGRID Gingiva Mask — Photopolymer resin for LCD/MSLA. Elongation at break 382 %

Kexcelled MOLEGRID GK One — Photopolymer resin for LCD/MSLA. Tensile strength 46 MPa · Elongation at break 21.2 %

Kexcelled MOLEGRID Head Sculpt — Photopolymer resin for LCD/MSLA. Tensile strength 45 MPa · Elongation at break 16 %

Kexcelled MOLEGRID Micro R Pro — Photopolymer resin for LCD/MSLA. Tensile strength 42 MPa · Elongation at break 16 %

Kexcelled MOLEGRID Model — Photopolymer resin for LCD/MSLA. Tensile strength 42 MPa

Kexcelled MOLEGRID Ortho Model — Photopolymer resin for LCD/MSLA. Tensile strength 44 MPa

Kexcelled MOLEGRID Rigid 130 — Photopolymer resin for LCD/MSLA. Tensile strength 66.3 MPa

Kexcelled MOLEGRID SG — Photopolymer resin for LCD/MSLA. Elongation at break 10 %

Kexcelled MOLEGRID Standard — Photopolymer resin for LCD/MSLA. Tensile strength 48 MPa · Elongation at break 12.17 %

Kexcelled MOLEGRID Study Model — Photopolymer resin for LCD/MSLA. Elongation at break 10 %

Kexcelled MOLEGRID Temp C&B — Photopolymer resin for LCD/MSLA

Kexcelled MOLEGRID Texture — Photopolymer resin for LCD/MSLA. Tensile strength 40 MPa · Elongation at break 13 %

Kexcelled MOLEGRID Tough 50 — Photopolymer resin for LCD/MSLA. Tensile strength 40 MPa · Elongation at break 50 %

Kexcelled MOLEGRID Tray — Photopolymer resin for LCD/MSLA. Elongation at break 12 %

Kexcelled MOLEGRID Try-in — Photopolymer resin for LCD/MSLA

Kexcelled MOLEGRID Washable — Photopolymer resin for LCD/MSLA. Tensile strength 42.83 MPa · Elongation at break 11.47 %

Kexcelled MOLEGRID Washable Model — Photopolymer resin for LCD/MSLA. Tensile strength 38.7 MPa

Kexcelled MOLEGRID X-PMMA — Photopolymer resin for LCD/MSLA. Tensile strength 32.55 MPa · Elongation at break 8.24 %

Kexcelled THE K10 PC — PC filament for FFF. Tensile strength 65–70 MPa · Young's modulus 3700–4000 MPa · Elongation at break 8–12 %

Kexcelled THE K10 PPS CF10 — PPS + Carbon Fiber filament for FFF. Tensile strength 86–92 MPa · Young's modulus 8200–8400 MPa · Elongation at break 3–5 %

Kexcelled THE K11 PEEK — PEEK filament for FFF. Tensile strength 70–80 MPa · Young's modulus 4200–4500 MPa · Elongation at break 4–6 %

Kexcelled THE K11 PEEK CF10 — PEEK + Carbon Fiber filament for FFF. Tensile strength 85–90 MPa · Young's modulus 7000–8000 MPa · Elongation at break 3–6 %

Kexcelled THE K11 PEEK GF10 — PEEK + Glass Fiber filament for FFF. Tensile strength 80–85 MPa · Young's modulus 7000–7500 MPa · Elongation at break 6–8 %

Kexcelled THE K11 PEEK PRO — PEEK filament for FFF. Tensile strength 72–75 MPa · Young's modulus 2600–2700 MPa · Elongation at break 15–17 %

Kexcelled THE K11 PEI 1010 — PEI filament for FFF. Tensile strength 85–90 MPa · Young's modulus 4500–5000 MPa · Elongation at break 4–6 %

Kexcelled THE K11 PEKK — PEKK filament for FFF. Tensile strength 80–100 MPa · Young's modulus 4200–4500 MPa · Elongation at break 4–6 %

Kexcelled THE K11 PPSU — PPSU filament for FFF. Tensile strength 50–60 MPa · Young's modulus 3200–3500 MPa · Elongation at break 10–12 %

Kexcelled THE K12 PEEK Ultra — PEEK filament for FFF. Tensile strength 75–90 MPa · Young's modulus 4500–5000 MPa · Elongation at break 11–15 %

Kexcelled THE K12 PEI 9085 — PEI filament for FFF. Tensile strength 70–75 MPa · Young's modulus 4000–4500 MPa · Elongation at break 6–8 %

Kexcelled THE K7 PET CF10 — PET + Carbon Fiber filament for FFF. Tensile strength 80–100 MPa · Young's modulus 6400–6900 MPa · Elongation at break 4–8 %

Kexcelled THE K8 TPU 64D — TPU filament for FFF. Tensile strength 30–35 MPa · Elongation at break 540–550 % · Density 1.22–1.24 g/cm³

Kexcelled THE K8 TPU 65A — TPU filament for FFF. Tensile strength >8 MPa · Elongation at break >2000 % · Density 1.20–1.22 g/cm³

Kexcelled THE K8 TPU 70A — TPU filament for FFF. Tensile strength >11 MPa · Elongation at break >2000 % · Density 1.15–1.17 g/cm³

Kexcelled THE K8 TPU 75A — TPU filament for FFF. Tensile strength >13 MPa · Elongation at break >2000 % · Density 1.21–1.23 g/cm³

Kexcelled THE K8 TPU 77D — TPU filament for FFF. Tensile strength 30–35 MPa · Elongation at break 370–400 % · Density 1.22–1.24 g/cm³

Kexcelled THE K8 TPU 80A — TPU filament for FFF. Tensile strength >24 MPa · Elongation at break >1600 % · Density 1.16–1.18 g/cm³

Kexcelled THE K8 TPU 85A — TPU filament for FFF. Tensile strength >24 MPa · Elongation at break >1400 % · Density 1.17–1.19 g/cm³

Kexcelled THE K8 TPU 90A — TPU filament for FFF. Tensile strength >36 MPa · Elongation at break >1400 % · Density 1.19–1.21 g/cm³

Kexcelled THE K8 TPU 90A M — TPU filament for FFF. Tensile strength 19–22 MPa · Elongation at break 570–590 % · Density 1.17–1.19 g/cm³

Kexcelled THE K8 TPU 95A — TPU filament for FFF. Tensile strength >34 MPa · Elongation at break >1100 % · Density 1.14–1.16 g/cm³

Kexcelled THE K8 TPU AIR — TPU filament for FFF. Tensile strength 14.8 (printed at 205 °C) MPa · Elongation at break 368.7 (printed at 205 °C) % · Density 1.14 (non-foaming) g/cm³

LEHVOSS LUVOCOM 3F PAHT 9825 — PA filament for FFF. Tensile strength 85 MPa · Young's modulus 3400 MPa · Elongation at break 3.6 %

LEHVOSS LUVOCOM 3F PAHT 9936 — PA6 filament for FFF. Tensile strength 78 MPa · Young's modulus 3400 MPa · Elongation at break 4.4 %

LEHVOSS LUVOCOM 3F PAHT CF 9742 — PA6 + Carbon Fiber 15% filament for FFF. Tensile strength 170 MPa · Young's modulus 15000 MPa · Elongation at break 1 %

LEHVOSS LUVOCOM 3F PAHT CF 9891 — PA6 + Carbon Fiber 15% filament for FFF. Tensile strength 130 MPa · Young's modulus 11500 MPa · Elongation at break 2 %

LEHVOSS LUVOCOM 3F PAHT KK 50056 FR — PA6 + Ceramic spheres filament for FFF. Tensile strength 55 MPa · Young's modulus 6000 MPa · Elongation at break 1.2 %

LEHVOSS LUVOCOM 3F PEEK 9581 — PEEK filament for FFF. Tensile strength 97 MPa · Young's modulus 3800 MPa · HDT 145 °C

LEHVOSS LUVOCOM 3F PEEK CF 9676 — PEEK + Carbon Fiber filament for FFF. Tensile strength 145 MPa · Young's modulus 10000 MPa · HDT 280 °C

LEHVOSS LUVOCOM 3F PEI 50236 — PEI filament for FFF. Tensile strength 105 MPa · Young's modulus 3500 MPa · Elongation at break 5 %

LEHVOSS LUVOCOM 3F PEKK 50082 — PEKK filament for FFF. Tensile strength 90 MPa · Young's modulus 3000 MPa · Elongation at break 5 %

LEHVOSS LUVOCOM 3F PPS CF 9938 — PPS + Carbon Fiber filament for FFF. Tensile strength 120 MPa · Young's modulus 11000 MPa · Density 1.51 g/cm³

Liqcreate Bio-Med Clear — Photopolymer resin for SLA/DLP/LCD. Tensile strength 55 MPa · Young's modulus 2000 MPa · Elongation at break 5–10 %

Liqcreate Bio-Med Flex — Photopolymer resin for SLA/DLP/LCD. Tensile strength 5.0 MPa · Elongation at break 180–250 %

Liqcreate Clear Impact — Photopolymer resin for SLA/DLP/LCD. Tensile strength 47 MPa · Young's modulus 1400 MPa · Elongation at break 15–25 %

Liqcreate Composite-X — Photopolymer + Nano-micro composite resin for SLA/DLP/LCD. Tensile strength 70–85 MPa · Young's modulus 8500–9500 MPa · Elongation at break 1 %

Liqcreate Deep Blue — Photopolymer resin for SLA/DLP/LCD. Tensile strength 73 MPa · Young's modulus 2600 MPa · Elongation at break 5 %

Liqcreate Dental Model Pro Beige — Photopolymer resin for SLA/DLP/LCD. Tensile strength 37 MPa · Young's modulus 1900 MPa · Elongation at break 4.8 %

Liqcreate Dental Model Pro Grey — Photopolymer resin for SLA/DLP/LCD. Tensile strength 49 MPa · Young's modulus 2300 MPa · Elongation at break 4.1 %

Liqcreate Elastomer-X — Photopolymer resin for SLA/DLP/LCD. Tensile strength 1.5 MPa · Elongation at break 140–180 % · Tg -5 °C

Liqcreate ESD — Photopolymer resin for SLA/DLP/LCD. Tensile strength 37 MPa · Young's modulus 1900 MPa · Elongation at break 5–10 %

Liqcreate Flame Retardant HDT — Photopolymer resin for SLA/DLP/LCD. Tensile strength 43 MPa · Young's modulus 4200 MPa · Elongation at break 1–3 %

Liqcreate Flexible-X — Photopolymer resin for SLA/DLP/LCD. Tensile strength 2.4 MPa · Elongation at break 120–160 %

Liqcreate Gingiva Mask — Photopolymer resin for SLA/DLP/LCD. Tensile strength 2.2 MPa · Elongation at break 80–120 %

Liqcreate Premium Black — Photopolymer resin for SLA/DLP/LCD. Tensile strength 45 MPa · Young's modulus 1000 MPa · Elongation at break 8 %

Liqcreate Premium Flex — Photopolymer resin for SLA/DLP/LCD. Tensile strength 1.7 MPa · Elongation at break 50–80 %

Liqcreate Premium Model — Photopolymer resin for SLA/DLP/LCD. Tensile strength 53 MPa · Young's modulus 1900 MPa · Elongation at break 4.1 %

Liqcreate Premium Tough — Photopolymer resin for SLA/DLP/LCD. Tensile strength 28 MPa · Young's modulus 1000 MPa · Elongation at break 15–25 %

Liqcreate Premium White — Photopolymer resin for SLA/DLP/LCD. Tensile strength 45 MPa · Young's modulus 1000 MPa · Elongation at break 8 %

Liqcreate Rigid Pro — Photopolymer resin for SLA/DLP/LCD. Tensile strength 52–70 MPa · Young's modulus 2600–2800 MPa · Elongation at break 4–8 %

Liqcreate Separation Model — Photopolymer resin for SLA/DLP/LCD

Liqcreate Stone Coal Black — Photopolymer resin for SLA/DLP/LCD. Tensile strength 62 MPa · Young's modulus 2200 MPa · Elongation at break 4 %

Liqcreate Strong-X — Photopolymer resin for SLA/DLP/LCD. Tensile strength 52–70 MPa · Young's modulus 2900–3200 MPa · Elongation at break 4–8 %

Liqcreate Tough-X — Photopolymer resin for SLA/DLP/LCD. Tensile strength 15 MPa · Elongation at break 100–150 % · HDT 41 °C

Liqcreate Tray — Photopolymer resin for SLA/DLP/LCD. Tensile strength 86 MPa · Young's modulus 2900 MPa · Elongation at break 2–4 %

Liqcreate Wax Castable — Photopolymer resin for SLA/DLP/LCD

Lubrizol ESTANE 3D TPU M88A-565 OR UV PW — TPU powder for MJF. Tensile strength 15 MPa · Elongation at break 440 % · Tg -31 °C

Lubrizol ESTANE 3D TPU M95A-545 OR UV — TPU powder for MJF. Tensile strength 17 MPa · Elongation at break 400 % · Density 1.10 - 1.15 g/cm³

Markforged 17-4PH Stainless Steel — 17-4 PH stainless steel filament for Metal FFF. Tensile strength 1230 MPa · Young's modulus 170000 MPa · Elongation at break 13 %

Markforged Carbon Fiber — + Carbon Fiber filament for FFF. Tensile strength 800 MPa · Young's modulus 60000 MPa · Elongation at break 1.5 %

Markforged Carbon Fiber FR — + Carbon Fiber filament for FFF. Tensile strength 760 MPa · Young's modulus 57000 MPa · Elongation at break 1.6 %

Markforged Carbon Fiber HT — + Carbon Fiber filament for FFF. Tensile strength 800 MPa · Young's modulus 69000 MPa · Elongation at break 1.6 %

Markforged Carbon Fiber HT-A — + Carbon Fiber filament for FFF. Tensile strength 800 MPa · Young's modulus 69000 MPa · Elongation at break 1.6 %

Markforged Copper — Copper filament for Metal FFF. Tensile strength 193 MPa · Elongation at break 45 %

Markforged D2 Tool Steel — D2 tool steel filament for Metal FFF. Young's modulus 178000 MPa

Markforged Fiberglass — + Glass Fiber filament for FFF. Tensile strength 590 MPa · Young's modulus 21000 MPa · Elongation at break 3.8 %

Markforged H13 Tool Steel — H13 tool steel filament for Metal FFF. Tensile strength 1540 MPa · Elongation at break 4 %

Markforged HSHT Fiberglass — + Glass Fiber filament for FFF. Tensile strength 600 MPa · Young's modulus 21000 MPa · Elongation at break 3.9 %

Markforged Inconel 625 — Inconel 625 filament for Metal FFF. Tensile strength 765 MPa · Elongation at break 42 %

Markforged Kevlar — + Aramid Fiber (Kevlar) filament for FFF. Tensile strength 610 MPa · Young's modulus 27000 MPa · Elongation at break 2.7 %

Markforged Nylon — Nylon filament for FFF. Tensile strength 36 MPa · Young's modulus 1700 MPa · Elongation at break 150 %

Markforged Nylon White FS — Nylon filament for FFF. Tensile strength 47 MPa · Young's modulus 1800 MPa · Elongation at break 23 %

Markforged Onyx — Nylon + Carbon Fiber filament for FFF. Tensile strength 37 MPa · Young's modulus 2400 MPa · Elongation at break 25 %

Markforged Onyx ESD — Nylon + Carbon Fiber filament for FFF. Tensile strength 52 (yield) MPa · Young's modulus 4200 MPa

Markforged Onyx FR — Nylon + Carbon Fiber filament for FFF. Tensile strength 46.7 ± 0.3 MPa · Young's modulus 3270 ± 80 MPa · Elongation at break 14.0 ± 0.4 %

Markforged Onyx GF — Nylon + Glass Fiber filament for FFF. Tensile strength 56.5 ± 0.9 MPa · Young's modulus 3100 ± 100 MPa · Elongation at break 6.2 ± 0.6 %

Markforged Precise PLA — PLA filament for FFF. Tensile strength 18 MPa · Young's modulus 2300 MPa · Elongation at break 27 %

Markforged Smooth TPU 95A — TPU filament for FFF. Tensile strength 26 MPa · Young's modulus 98 (at 2% strain) MPa · Elongation at break 550 %

Markforged ULTEM 9085 Filament — Filament for FFF. Tensile strength 76.5 ± 5.0 MPa · Young's modulus 2500 ± 100 MPa · Elongation at break 5.7 ± 1.0 %

Markforged Vega — PEKK + Carbon Fiber filament for FFF. Tensile strength 87.6 ± 3.0 MPa · Young's modulus 5200 ± 200 MPa · Elongation at break 3.0 ± 0.2 %

Monocure3D BioResin — Photopolymer resin for LCD/MSLA. Tensile strength 49 MPa · Young's modulus 1800 MPa · HDT 130 °C

Monocure3D CAST — Photopolymer resin for LCD/MSLA. Tensile strength 40 MPa · Young's modulus 1500 MPa · Elongation at break 3 %

Monocure3D Denture Base Resin — Photopolymer resin for LCD/MSLA. Tensile strength 61–72 MPa · Elongation at break 20 %

Monocure3D Flex45A — Photopolymer resin for LCD/MSLA. Tensile strength 1.1 MPa · Elongation at break 165.5 %

Monocure3D Gingiva — Photopolymer resin for LCD/MSLA. Tensile strength 2.7 MPa · Elongation at break 36 % · HDT 45 °C

Monocure3D Guide — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Elongation at break 3.0 % · HDT 130 °C

Monocure3D HeatResist — Photopolymer resin for LCD/MSLA. Tensile strength 58 MPa · Young's modulus 1700 MPa · Elongation at break 5.0 %

Monocure3D Impact — Photopolymer resin for LCD/MSLA. Tensile strength 65 MPa · Young's modulus 1300 MPa · Elongation at break 15.0 %

Monocure3D Mini — Photopolymer resin for LCD/MSLA. Tensile strength 55 MPa · Young's modulus 1200 MPa · Elongation at break 10.0 %

Monocure3D Precise+ — Photopolymer resin for LCD/MSLA. Tensile strength 64 MPa · Elongation at break 3.0 % · HDT 71 °C

Monocure3D Pro+ — Photopolymer resin for LCD/MSLA. Tensile strength 68 MPa · Young's modulus 950 MPa · Elongation at break 3.8 %

Monocure3D Proto — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Young's modulus 1800 MPa · Elongation at break 3.0 %

Monocure3D Splint Hard — Photopolymer resin for LCD/MSLA. Tensile strength 61–72 MPa · Elongation at break 20 %

Monocure3D Splint Soft — Photopolymer resin for LCD/MSLA. Tensile strength 46–52 MPa · Elongation at break 105 %

Monocure3D Study — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Elongation at break 3.0 % · HDT 55 °C

Monocure3D Tensile — Photopolymer resin for LCD/MSLA. Tensile strength 86.7 MPa · Young's modulus 1400 MPa · Elongation at break 2.5 %

Monocure3D ThermaCAST — Photopolymer resin for LCD/MSLA. Tensile strength 45 MPa · Elongation at break 1–2 % · HDT 150 °C

Monocure3D Thermo — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Elongation at break 3.0 % · HDT 130 °C

Monocure3D Tray — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Elongation at break 3.0 % · HDT 130 °C

Monocure3D Try-In — Photopolymer resin for LCD/MSLA. Tensile strength 47 MPa · Elongation at break 3.0 % · HDT 130 °C

Panchroma CoPE — Filament for FFF. Tensile strength 51.6 ± 0.3 MPa · Young's modulus 2515 ± 71 MPa · Density 1.30 g/cm³

Panchroma Matte — Filament for FFF. Tensile strength 23.2 ± 0.5 MPa · Young's modulus 1997 ± 64 MPa · Density 1.37 g/cm³

Panchroma Others — Filament for FFF. Tensile strength 52.3 ± 0.3 MPa · Young's modulus 3427 ± 65 MPa · Density 1.17 g/cm³

Panchroma Satin — Filament for FFF. Tensile strength 31.1 ± 0.8 MPa · Young's modulus 2246 ± 91 MPa · Density 1.24 g/cm³

Panchroma Silk — Filament for FFF. Tensile strength 41.1 ± 0.8 MPa · Young's modulus 2403 ± 74.5 MPa · Density 1.24 g/cm³

Phrozen ABS-like Resin — Photopolymer resin for LCD/MSLA. Tensile strength 29.6–33.3 MPa · Young's modulus 1644.2–1742 MPa · Elongation at break 5.6–5.8 %

Phrozen Aqua 4K Resin — Photopolymer resin for LCD/MSLA. Tensile strength 26–28 MPa · Young's modulus 1260–1520 MPa · Elongation at break 15.6–18.3 %

Phrozen Aqua 8K Resin — Photopolymer resin for LCD/MSLA. Tensile strength 35–46 MPa · Young's modulus 2433–2848 MPa · Elongation at break 4.8–7.6 %

Phrozen Aqua Clear Plus — Photopolymer resin for LCD/MSLA. Tensile strength 34 MPa · Young's modulus 2277.3 MPa · Elongation at break 13.6 %

Phrozen Aqua Mist-Gray — Photopolymer resin for LCD/MSLA. Tensile strength 17.6 MPa · Young's modulus 1435 MPa · Elongation at break 1.26 %

Phrozen Aqua Oat-White — Photopolymer resin for LCD/MSLA. Tensile strength 38.5 MPa · Young's modulus 1955 MPa · Elongation at break 3.17 %

Phrozen BJD Resin Ivory — Photopolymer resin for LCD/MSLA. Tensile strength 28.7 MPa · Young's modulus 1538.3 MPa · Elongation at break 11.5 %

Phrozen BJD Soft Light Blush Ivory — Photopolymer resin for LCD/MSLA. Young's modulus 2.4 MPa · Elongation at break 106.2 %

Phrozen Ceramic Pro — Photopolymer + Ceramic-filled resin for LCD/MSLA. Tensile strength 83.8 MPa · Young's modulus 8380 MPa · Elongation at break 1 %

Phrozen Ceramic White — Photopolymer resin for LCD/MSLA. Tensile strength 49.6 MPa · Young's modulus 4320 MPa · Elongation at break 2 %

Phrozen EL400 — Photopolymer resin for LCD/MSLA. Tensile strength 6.3 MPa · Elongation at break 391 %

Phrozen FR940 — Acrylic resin for LCD/MSLA. Tensile strength 28.5 MPa · Young's modulus 1812 MPa · Elongation at break 3.8 %

Phrozen Hyperfine Resin — Photopolymer resin for LCD/MSLA. Tensile strength 32.0–38.7 MPa · Young's modulus 1614–2104 MPa · Elongation at break 2.9–6.6 %

Phrozen Macaron Resin — Photopolymer resin for LCD/MSLA. Tensile strength 27.9–34.9 MPa · Young's modulus 1286–1826 MPa · Elongation at break 4.2–8.5 %

Phrozen Neon — Photopolymer resin for LCD/MSLA. Tensile strength 19–23 MPa · Young's modulus 800–1150 MPa · Elongation at break 3–12 %

Phrozen Nylon Green — Photopolymer resin for LCD/MSLA. Tensile strength 21.2 MPa · Young's modulus 836.2 MPa · Elongation at break 83.3 %

Phrozen Onyx Impact Plus — Photopolymer resin for LCD/MSLA. Tensile strength 30.6 MPa · Young's modulus 943.1 MPa · Elongation at break 90.9 %

Phrozen Onyx Rigid Pro410 — Photopolymer resin for LCD/MSLA. Tensile strength 36.4 MPa · Young's modulus 1882.8 MPa · Elongation at break 9.3 %

Phrozen PC/GF-like — Photopolymer resin for LCD/MSLA. Tensile strength 63 MPa · Young's modulus 3330 MPa · Elongation at break 5.5 %

Phrozen Protowhite — Photopolymer resin for LCD/MSLA. Tensile strength 57 MPa · Young's modulus 2300 MPa · Elongation at break 15 %

Phrozen Rock-Black Stiff — Photopolymer resin for LCD/MSLA. Tensile strength 46.3 MPa · Young's modulus 3105 MPa · Elongation at break 16.7 %

Phrozen RPG Series — Photopolymer resin for LCD/MSLA. Tensile strength 21.7–24.2 MPa · Young's modulus 959.8–1152.3 MPa · Elongation at break 25.3–30.6 %

Phrozen Speed Gray — Photopolymer resin for LCD/MSLA. Tensile strength 45.5 MPa · Young's modulus 3019.7 MPa · Elongation at break 12.9 %

Phrozen Speed Plus Black — Photopolymer resin for LCD/MSLA. Tensile strength 43.6 MPa · Young's modulus 2414 MPa · Elongation at break 5.7 %

Phrozen Tough 100E Black — Photopolymer resin for LCD/MSLA. Tensile strength 24.6 MPa · Young's modulus 925.4 MPa · Elongation at break 100.5 %

Phrozen Tough 100E Green — Photopolymer resin for LCD/MSLA. Tensile strength 29.9 MPa · Young's modulus 1058.8 MPa · Elongation at break 93.5 %

Phrozen Tough ABS Like + — Photopolymer resin for LCD/MSLA. Tensile strength 35.8 MPa · Young's modulus 2490 MPa · Elongation at break 17.7 %

Phrozen TR250LV — Photopolymer resin for LCD/MSLA. Tensile strength 50.8 MPa · Young's modulus 2784.5 MPa · Elongation at break 7.4 %

Phrozen TR300 — Photopolymer resin for LCD/MSLA. Tensile strength 87.7 MPa · Young's modulus 4883.3 MPa · Elongation at break 2.2 %

Phrozen Water-Washable — Photopolymer resin for LCD/MSLA. Tensile strength 11–25.5 MPa · Young's modulus 486.2–1383 MPa · Elongation at break 3.5–8.3 %

Phrozen Water-Washable Tough — Photopolymer resin for LCD/MSLA. Tensile strength 22.4–22.9 MPa · Young's modulus 863.4–993 MPa · Elongation at break 16.3–23.1 %

PolyLite LW-PLA — PLA filament for FFF. Tensile strength 24.4 ± 0.3 MPa · Young's modulus 1688.5 ± 80.8 MPa · Elongation at break 8.8 ± 0.3 %

Polymaker ABS-Max — ABS filament for FFF. Tensile strength 35.66 ± 0.58 MPa · Young's modulus 2320 ± 30 MPa · Elongation at break 6.72 ± 0.34 %

Polymaker ABS-Pro — ABS filament for FFF. Tensile strength 34.94 ± 0.62 MPa · Young's modulus 2330 ± 30 MPa · Elongation at break 7.34 ± 1.13 %

Polymaker ASA — ASA filament for FFF. Tensile strength 43.8 ± 0.8 MPa · Young's modulus 2379 ± 157 MPa · Elongation at break 6.7 ± 0.6 %

Polymaker HT-PLA — PLA filament for FFF. Tensile strength 42.86 ± 0.76 MPa · Young's modulus 2945.75 ± 77.35 MPa · Elongation at break 2.80 ± 0.26 %

Polymaker HT-PLA-GF — PLA + Glass Fiber filament for FFF. Tensile strength 50.09 ± 0.73 MPa · Young's modulus 3793.85 ± 129.17 MPa · Elongation at break 2.77 ± 0.45 %

Polymaker PC-ABS — PC/ABS filament for FFF. Tensile strength 39.9 ± 1.0 MPa · Young's modulus 1835 ± 65 MPa · Elongation at break 4.2 ± 0.3 %

Polymaker PC-PBT — PC/PBT filament for FFF. Tensile strength 50.4 ± 0.6 MPa · Young's modulus 1940.2 ± 76.5 MPa · Elongation at break 4.6 ± 0.7 %

Polymaker PETG — PETG filament for FFF. Tensile strength 47.96 ± 4.88 MPa · Young's modulus 2311.11 ± 92.41 MPa · Elongation at break 9.33 ± 6.57 %

Polymaker PLA-Pro — PLA filament for FFF. Tensile strength 39.93 ± 0.44 MPa · Young's modulus 2531.08 ± 25.16 MPa · Elongation at break 16.57 ± 6.18 %

Polymaker Polycast — PVB filament for FFF. Tensile strength 53.2 ± 1.1 MPa · Young's modulus 2215 ± 42 MPa · Elongation at break 5.7 ± 0.5 %

Polymaker PolyCore ABS-5012 — ABS + Glass Fiber 20% pellets for Pellet extrusion. Tensile strength 74.6 ± 3.8 MPa · Young's modulus 3994 ± 159 MPa · Elongation at break 9.7 ± 0.7 %

Polymaker PolyCore ABS-5022 — ABS + Carbon Fiber 20% pellets for Pellet extrusion. Tensile strength 90 ± 3.0 MPa · Young's modulus 8093 ± 1457 MPa · Elongation at break 0.7 ± 0.2 %

Polymaker PolyCore ASA-3000 — ASA pellets for Pellet extrusion. Tensile strength 43.8 ± 0.8 MPa · Young's modulus 2379 ± 157 MPa · Elongation at break 6.7 ± 0.6 %

Polymaker PolyCore ASA-3012 — ASA + Glass Fiber 20% pellets for Pellet extrusion. Tensile strength 55.9 ± 4.2 MPa · Young's modulus 5394 ± 441 MPa · Elongation at break 1.4 ± 0.2 %

Polymaker PolyCore PC-7413 — PC pellets for Pellet extrusion. Tensile strength 74.6 ± 1.9 MPa · Young's modulus 4752 ± 175 MPa · Elongation at break 2.39 ± 0.14 %

Polymaker PolyCore PETG-1000 — PETG pellets for Pellet extrusion. Tensile strength 37.4 ± 5.8 MPa · Young's modulus 1744 ± 105 MPa · Elongation at break 11.2 ± 2.7 %

Polymaker PolyCore PETG-1013 — PETG + Glass Fiber 30% pellets for Pellet extrusion. HDT 77 °C · Tg 81 °C · Density 1.39 g/cm³

Polymaker PolyCore PETG-1113 Marble — PETG + Glass Fiber 30% pellets for Pellet extrusion. Tensile strength 100.3 ± 0.9 MPa · Young's modulus 8186 ± 157 MPa · Elongation at break 2.2 ± 0.2 %

Polymaker PolyCore PETG-1211 — PETG + Glass Fiber 10% pellets for Pellet extrusion. Tensile strength 68.1 ± 0.8 MPa · Young's modulus 3288 ± 85 MPa · Elongation at break 3.5 ± 0.42 %

Polymaker PolyCore TPU-2000 — TPU pellets for Pellet extrusion. Tensile strength 36.9 ± 3.2 MPa · Elongation at break 558.5 ± 57.8 % · Density 1.3 g/cm³

Polymaker PolyDissolveS1 — HIPS filament for FFF. Density 1.13 g/cm³

Polymaker PolyFlex-TPU90 — TPU filament for FFF. Elongation at break 592.1 ± 32.9 % · Density 1.21 at 23 g/cm³

Polymaker PolyFlex-TPU95 — TPU filament for FFF. Elongation at break 551.2 ± 23.5 % · Density 1.20 g/cm³ at 23

Polymaker PolyFlex-TPU95-HF — TPU filament for FFF. Tensile strength 26.6 ± 0.6 MPa · Elongation at break 495.8 ± 16.2 % · Density 1.16 at 3 g/cm³

Polymaker PolyLite-ABS — ABS filament for FFF. Tensile strength 33.4 ± 92.7 MPa · Young's modulus 2246.6 ± 58.2 MPa · Elongation at break 17.9 ± 1.3 %

Polymaker PolyLite-CosPLA-Version-A — PLA filament for FFF. Tensile strength 31.1 ± 0.8 MPa · Young's modulus 2245.9 ± 90.7 MPa · Elongation at break 13.8 ± 2.9 %

Polymaker PolyLite-CosPLA-Version-B — PLA filament for FFF. Tensile strength 49.8 ± 0.9 MPa · Young's modulus 2932.2 ± 55.3 MPa · Elongation at break 6.3 ± 0.9 %

Polymaker PolyLite-PC-Transparent — PC filament for FFF. Tensile strength 69.1 ± 3.0 MPa · Young's modulus 2497 ± 154 MPa · Elongation at break 4.8 ± 0.9 %

Polymaker PolyLite-PETG — PETG filament for FFF. Tensile strength 50.8 ± 0.9 MPa · Young's modulus 2116.8 ± 68.1 MPa · Elongation at break 8.4 ± 1.7 %

Polymaker Polylite-PLA-CF — PLA + Carbon Fiber filament for FFF. Tensile strength 31.2 ± 0.7 MPa · Young's modulus 3280.7 ± 79.6 MPa · Elongation at break 13.2 ± 1.7 %

Polymaker PolyLite-PLA-Pro — PLA filament for FFF. Tensile strength 49.8 ± 0.4 MPa · Young's modulus 2932.2 ± 55.3 MPa · Elongation at break 6.3 ± 0.9 %

Polymaker PolyMax-PC — PC filament for FFF. Tensile strength 53.44 ± 0.60 MPa · Young's modulus 2435 ± 63 MPa · Elongation at break 4.53 ± 0.45 %

Polymaker PolyMax-PC-FR — PC filament for FFF. Tensile strength 67 ± 4.5 MPa · Young's modulus 2634 ± 182 MPa · Elongation at break 3.49 ± 0.7 %

Polymaker PolyMax-PETG — PETG filament for FFF. Tensile strength 37.9 ± 1.4 MPa · Young's modulus 1684 ± 135 MPa · Elongation at break 5.22 ± 1.5 %

Polymaker PolyMax-PLA — PLA filament for FFF. Tensile strength 41.3 ± 2.2 MPa · Young's modulus 2150.8 ± 67.8 MPa · Elongation at break 5.7 ± 0.8 %

Polymaker PolyMide-CoPA — PA6,66 filament for FFF. Tensile strength 78.0 ± 0.7 MPa · Young's modulus 2703 ± 259 MPa · Elongation at break 12.7 ± 2.1 %

Polymaker PolySmooth — PVB filament for FFF. Tensile strength 51.8 ± 0.7 MPa · Young's modulus 2199 ± 43 MPa · Elongation at break 14.5 ± 2.9 %

Polymaker PolySonic-PLA-Pro — PLA filament for FFF. Tensile strength 41.2 ± 0.6 MPa · Young's modulus 2360.0 ± 30.1 MPa · Elongation at break 23.4 ± 6.3 %

Polymaker PolySupport — PVA filament for FFF. Density 1.22 g/cm³

Polymaker PolySupport-PA12 — PA12 filament for FFF. HDT 53 °C · Density 1.29 g/cm³

Polymaker Polywood-PLA — PLA filament for FFF. Tensile strength 24.4 ± 0.3 MPa · Young's modulus 1688.5 ± 80.8 MPa · Elongation at break 8.8 ± 0.3 %

PolySonic PLA — PLA filament for FFF. Tensile strength 46.0 ± 0.5 MPa · Young's modulus 2878.3 ± 74.3 MPa · Elongation at break 21.5 ± 5.1 %

PolyTerra PLA — PLA filament for FFF. Tensile strength 23.2 ± 0.5 MPa · Young's modulus 1997 ± 64 MPa · Elongation at break 27.8 ± 2.4 %

Siraya Tech Blu — Photopolymer resin for LCD/MSLA. Tensile strength 50 MPa · Young's modulus 1800 MPa · Elongation at break 32 %

Siraya Tech Blu Easy — Photopolymer resin for LCD/MSLA. Tensile strength 31 MPa · Young's modulus 1000 MPa · Elongation at break 43 %

Siraya Tech Blu Lava — Photopolymer resin for LCD/MSLA. Tensile strength 60 MPa · Young's modulus 2500 MPa · Elongation at break 12 %

Siraya Tech Blu Nylon — Photopolymer resin for LCD/MSLA. Tensile strength 45 MPa · Young's modulus 1750 MPa · Elongation at break 50 %

Siraya Tech Blu Nylon Mecha — Photopolymer resin for LCD/MSLA. Tensile strength 58 MPa · Young's modulus 1900 MPa · Elongation at break 45 %

Siraya Tech Build — Photopolymer resin for LCD/MSLA. Tensile strength 33 MPa · Young's modulus 850 MPa · Elongation at break 8 %

Siraya Tech Cast Purple — Photopolymer resin for LCD/MSLA. Tensile strength 20 MPa · Young's modulus 600 MPa · Elongation at break 5 %

Siraya Tech Cast True Blue/Royal Blue — Photopolymer resin for LCD/MSLA. Tensile strength 20 MPa · Young's modulus 600 MPa · Elongation at break 4 %

Siraya Tech Craft Ultra Clear — Photopolymer resin for LCD/MSLA. Tensile strength 38 MPa · Young's modulus 1200 MPa · Elongation at break 6 %

Siraya Tech Fast — Photopolymer resin for LCD/MSLA. Young's modulus 1700 MPa · Elongation at break 18 % · HDT 65 °C

Siraya Tech Fast Mecha — Photopolymer resin for LCD/MSLA. Tensile strength 30 MPa · Young's modulus 1050 MPa · Elongation at break 23 %

Siraya Tech Fast Tough — Photopolymer resin for LCD/MSLA. Tensile strength 32 MPa · Young's modulus 1050 MPa · Elongation at break 40 %

Siraya Tech Magna Durable — Photopolymer resin for LCD/MSLA. Tensile strength 44 MPa · Young's modulus 1750 MPa · Elongation at break 65 %

Siraya Tech Rebound 55A — Photopolymer resin for LCD/MSLA. Density 1.2 g/cm³

Siraya Tech Sculpt — Photopolymer resin for LCD/MSLA. Young's modulus 3500 MPa · Elongation at break 5 % · HDT 160 °C

Siraya Tech Sculpt Ultra White — Photopolymer resin for LCD/MSLA. Tensile strength 31 MPa · Young's modulus 8000 MPa · Elongation at break 1 %

Siraya Tech Simple — Photopolymer resin for LCD/MSLA. Tensile strength 25 MPa · Young's modulus 650 MPa · Elongation at break 4 %

Siraya Tech Simple V2 — Photopolymer resin for LCD/MSLA. Tensile strength 27 MPa · Young's modulus 750 MPa · Elongation at break 10 %

Siraya Tech Tenacious 65D — Photopolymer resin for LCD/MSLA. Tensile strength 28 MPa · Young's modulus 800 MPa · Elongation at break 70 %

Siraya Tech Tenacious Easy — Photopolymer resin for LCD/MSLA. Tensile strength 34 MPa · Young's modulus 950 MPa · Elongation at break 55 %

Siraya Tech Tenacious Flex 70A — Photopolymer resin for LCD/MSLA. Tensile strength 5 MPa · Young's modulus 10 MPa · Elongation at break 140 %

Siraya Tech Tenacious Lava — Photopolymer resin for LCD/MSLA. Tensile strength 46 MPa · Young's modulus 1800 MPa · Elongation at break 75 %

Somos 9120 — Photopolymer resin for SLA. Tensile strength 31 MPa · Young's modulus 1350 MPa · Density ~1.13 g/cm³

Somos BioClear — Photopolymer resin for SLA. Tensile strength 50.4 MPa · Young's modulus 2770 MPa · Elongation at break 15.5 %

Somos EvoLVe 128 — Photopolymer resin for SLA. Tensile strength 56.8 MPa · Young's modulus 2964 MPa · Elongation at break 11 %

Somos Taurus — Photopolymer resin for SLA. Tensile strength 46.9 MPa · Young's modulus 2310 MPa · Elongation at break 24 %

Somos WaterClear Ultra 10122 — Photopolymer resin for SLA. Tensile strength 56 MPa · Young's modulus 2880 MPa · Elongation at break 7.5 %

Somos WaterShed Black — Photopolymer resin for SLA. Tensile strength 35 ± 5 MPa · Young's modulus 2300 ± 300 MPa · Elongation at break 12 ± 3 %

Somos WaterShed XC 11122 — Photopolymer resin for SLA. Tensile strength 50.4 MPa · Young's modulus 2770 MPa · Elongation at break 15.5 %

Stratasys ABS-M30 — ABS filament for FFF. Tensile strength 28.1 ± 0.58 MPa · Young's modulus 2400 ± 80 MPa · Elongation at break 8.1 ± 1.5 %

Stratasys Agilus30 — Photopolymer resin for PolyJet. Tensile strength 2.4 – 3.1 MPa · Elongation at break 220 – 240 % · Density 1.14 – 1.15 g/cm³

Stratasys ASA — ASA filament for FFF. Tensile strength 31.9 ± 0.98 MPa · Young's modulus 2140 ± 72 MPa · Elongation at break 5.9 ± 0.76 %

Stratasys Digital ABS Plus — Photopolymer resin for PolyJet. Tensile strength 55 – 60 MPa · Young's modulus 2600 – 3000 MPa · Elongation at break 25 – 40 %

Stratasys MED610 Biocompatible Clear — Photopolymer resin for PolyJet. Tensile strength 50 – 65 MPa · Young's modulus 2000 – 3000 MPa · Elongation at break 10 – 25 %

Stratasys MED615RGD Biocompatible Opaque — Photopolymer resin for PolyJet. Tensile strength 55 – 65 MPa · Young's modulus 2300 – 3300 MPa · Elongation at break 10 – 25 %

Stratasys Nylon 12 — PA12 filament for FFF. Tensile strength 33.4 ± 1.7 MPa · Young's modulus 1510 ± 87 MPa · Elongation at break 30 ± 23 %

Stratasys Nylon 12CF — PA12 + Carbon Fiber 35% filament for FFF. Tensile strength 83.5 ± 1.7 MPa · Young's modulus 9460 ± 460 MPa · Elongation at break 2.4 ± 0.29 %

Stratasys Nylon 6 — PA6 filament for FFF. Tensile strength 67.6 MPa · Young's modulus 2232 MPa · Elongation at break 38 %

Stratasys PC — PC filament for FFF. Tensile strength 54.1 ± 11 MPa · Young's modulus 2940 ± 50 MPa · Elongation at break 12 %

Stratasys PC-ABS — PC/ABS filament for FFF. Tensile strength 34.7 ± 0.83 MPa · Young's modulus 1990 ± 38 MPa · Elongation at break 4.7 ± 0.75 %

Stratasys PC-ISO — PC filament for FFF. Tensile strength 57 MPa · Young's modulus 2000 MPa · Elongation at break 4 %

Stratasys PolyJet Flex FLX9740/FLX9840 — Photopolymer resin for PolyJet. Tensile strength 3 – 4 MPa · Elongation at break 190 – 210 %

Stratasys PolyJet Flex FLX9750/FLX9850 — Photopolymer resin for PolyJet. Tensile strength 3 – 4 MPa · Elongation at break 170 – 210 %

Stratasys PolyJet Flex FLX9760/FLX9860 — Photopolymer resin for PolyJet. Tensile strength 3.5 – 4.5 MPa · Elongation at break 150 – 170 %

Stratasys PolyJet Flex FLX9770/FLX9870 — Photopolymer resin for PolyJet. Tensile strength 4 – 6 MPa · Elongation at break 120 – 140 %

Stratasys PolyJet Flex FLX9785/FLX9885 — Photopolymer resin for PolyJet. Tensile strength 6 – 10 MPa · Elongation at break 70 – 90 %

Stratasys PolyJet Flex FLX9795/FLX9895 — Photopolymer resin for PolyJet. Tensile strength 10 – 14 MPa · Elongation at break 50 – 70 %

Stratasys PPSF — PPSU filament for FFF. Tensile strength 55 MPa · Young's modulus 2100 MPa · Elongation at break 3 %

Stratasys ToughONE White — Photopolymer resin for PolyJet. Tensile strength 40 ± 2 MPa · Young's modulus 2433 ± 185 MPa · Elongation at break 55 ± 4 %

Stratasys ToughONE WhiteS — Photopolymer resin for PolyJet. Tensile strength 39 ± 3 MPa · Young's modulus 2229 ± 151 MPa · Elongation at break 40 ± 10 %

Stratasys ULTEM 1010 Resin — PEI filament for FFF. Tensile strength 79.2 ± 4.9 MPa · Young's modulus 3040 ± 180 MPa · Elongation at break 4.0 ± 0.42 %

Stratasys ULTEM 9085 Resin — PEI filament for FFF. Tensile strength 68.1 ± 1.6 MPa · Young's modulus 2520 ± 62 MPa · Elongation at break 5.4 ± 0.50 %

Stratasys Vero — Photopolymer resin for PolyJet. Tensile strength 50 – 65 MPa · Young's modulus 2000 – 3000 MPa · Elongation at break 10 – 25 %

Stratasys VeroBlue — Photopolymer resin for PolyJet. Tensile strength 50 – 60 MPa · Young's modulus 2000 – 3000 MPa · Elongation at break 15 – 25 %

Stratasys VeroUltraClear — Photopolymer resin for PolyJet. Tensile strength 39 – 43 MPa · Young's modulus 1400 – 2100 MPa · Elongation at break 20 – 35 %

Ultracur3D DM 2505 — Photopolymer resin for DLP/SLA. Tensile strength 48 MPa · Young's modulus 2200 MPa · Elongation at break 4 %

Ultracur3D DM 4505 N — Photopolymer resin for DLP/SLA. Tensile strength 55 MPa · Young's modulus 2500 MPa · Elongation at break 5 %

Ultracur3D EL 4000 — Photopolymer resin for DLP/SLA. Tensile strength 11 MPa · Elongation at break 170 % · Tg -15 °C

Ultracur3D EL 4000 B — Photopolymer resin for DLP/SLA. Tensile strength 13 MPa · Elongation at break 160 % · Tg -9.4 °C

Ultracur3D EL 60 — Photopolymer resin for DLP/SLA. Tensile strength 9 MPa · Elongation at break 95 % · Tg 29 °C

Ultracur3D EPD 1086 — Photopolymer resin for DLP/SLA. Tensile strength 42 MPa · Young's modulus 1810 MPa · Elongation at break 26 %

Ultracur3D EPD 2006 — Photopolymer resin for DLP/SLA. Tensile strength 50 MPa · Young's modulus 2370 MPa · Elongation at break 10.3 %

Ultracur3D FL 300 — Photopolymer resin for DLP/SLA. Tensile strength 5 MPa · Elongation at break 245 % · Tg -13 °C

Ultracur3D RG 1100 — Photopolymer resin for DLP/SLA. Tensile strength 70 MPa · Young's modulus 3080 MPa · Elongation at break 5 %

Ultracur3D RG 1100 B — Photopolymer resin for DLP/SLA. Tensile strength 70 MPa · Young's modulus 2950 MPa · Elongation at break 5 %

Ultracur3D RG 3280 — Photopolymer + Ceramic filler resin for DLP/SLA. Tensile strength 87 MPa · Young's modulus 10600 MPa · Elongation at break 1.3 %

Ultracur3D RG 35 — Photopolymer resin for DLP/SLA. Tensile strength 80 MPa · Young's modulus 2600 MPa · Elongation at break 6 %

Ultracur3D RG 35 B — Photopolymer resin for DLP/SLA. Tensile strength 62 MPa · Young's modulus 2600 MPa · Elongation at break 10 %

Ultracur3D RG 9400 B FR — Photopolymer resin for DLP/SLA. Tensile strength 78 MPa · Young's modulus 3900 MPa · Elongation at break 3 %

Ultracur3D SLA 7700 — Photopolymer resin for SLA. Tensile strength 46-51 MPa · Young's modulus 2250-2550 MPa · Elongation at break 5-15 %

Ultracur3D ST 45 — Photopolymer resin for DLP/SLA. Tensile strength 60 MPa · Young's modulus 2300 MPa · Elongation at break 25 %

Ultracur3D ST 45 B — Photopolymer resin for DLP/SLA. Tensile strength 53 MPa · Young's modulus 2000 MPa · Elongation at break 21 %

Ultracur3D ST 45 M — Photopolymer resin for DLP/SLA. Tensile strength 58 MPa · Young's modulus 2300 MPa · Elongation at break 20 %

Ultracur3D ST 7500 G — Photopolymer resin for DLP/SLA. Tensile strength 54 MPa · Young's modulus 2300 MPa · Elongation at break 13 %

Ultrafuse 17-4PH — 17-4 PH stainless steel filament for Metal FFF. Tensile strength 990 MPa · Young's modulus 191000 MPa · Elongation at break 4 %

Ultrafuse 316L — 316L stainless steel filament for Metal FFF. Tensile strength 561 MPa · Elongation at break 53 % · Density 7.850 g/cm³

Ultrafuse ABS — ABS filament for FFF. Tensile strength 36.3 MPa · Young's modulus 1958 MPa · Elongation at break 7.4 %

Ultrafuse ABS Fusion+ — ABS filament for FFF. Tensile strength 28.3 MPa · Young's modulus 1445 MPa · Elongation at break 7.0 %

Ultrafuse ASA — ASA filament for FFF. Tensile strength 34.6 MPa · Young's modulus 1828 MPa · Elongation at break 4.5 %

Ultrafuse BVOH — BVOH filament for FFF. Tensile strength 33.7 MPa · Young's modulus 2339 MPa · Elongation at break 14.8 %

Ultrafuse PA6 GF30 — PA6 + Glass Fiber filament for FFF. Tensile strength 78.3 MPa · Young's modulus 5036 MPa · Elongation at break 2.2 %

Ultrafuse PAHT CF15 — PAHT + Carbon Fiber filament for FFF. Tensile strength 103.2 MPa · Young's modulus 8386 MPa · Elongation at break 1.8 %

Ultrafuse PC GF30 — PC + Glass Fiber filament for FFF. Tensile strength 36.1 MPa · Young's modulus 2665 MPa · Elongation at break 2.4 %

Ultrafuse PC/ABS FR Black — PC/ABS filament for FFF. Tensile strength 50.1 MPa · Young's modulus 2545 MPa · Elongation at break 10.7 %

Ultrafuse Pellets PC GF30 — PC + Glass Fiber 30% pellets for Pellet extrusion. Tensile strength 36.1 MPa · Young's modulus 2665 MPa · Elongation at break 2.4 %

Ultrafuse Pellets PP GF30 — PP + Glass Fiber 30% pellets for Pellet extrusion. Tensile strength 41.7 MPa · Young's modulus 2628 MPa · Elongation at break 4.4 %

Ultrafuse Pellets rPETG — PETG pellets for Pellet extrusion. Tensile strength 38.6 MPa · Young's modulus 1640 MPa · Elongation at break 4.3 %

Ultrafuse PET — PET filament for FFF. Tensile strength 33.4 MPa · Young's modulus 1933 MPa · Elongation at break 2.7 %

Ultrafuse PET CF15 — PET + Carbon Fiber filament for FFF. Tensile strength 63.2 MPa · Young's modulus 6178 MPa · Elongation at break 3.7 %

Ultrafuse PLA — PLA filament for FFF. Tensile strength 34.7 MPa · Young's modulus 2308 MPa · Elongation at break 4.2 %

Ultrafuse PLA Pro1 — PLA filament for FFF. Tensile strength 48.0 MPa · Young's modulus 3166 MPa · Elongation at break 21.9 %

Ultrafuse PLA Tough — PLA filament for FFF. Tensile strength 40 MPa · Young's modulus 2672 MPa · Elongation at break 7.4 %

Ultrafuse PP — PP filament for FFF. Tensile strength 15.5 MPa · Young's modulus 541 MPa · Elongation at break 118.6 %

Ultrafuse PP GF30 — PP + Glass Fiber 30% filament for FFF. Tensile strength 41.7 MPa · Young's modulus 2628 MPa · Elongation at break 4.4 %

Ultrafuse PPSU — PPSU filament for FFF. Tensile strength 74.5 MPa · Young's modulus 2221 MPa · Elongation at break 7.3 %

Ultrafuse rPET — PET filament for FFF. Tensile strength 38.6 MPa · Young's modulus 1640 MPa · Elongation at break 4.3 %

Ultrafuse Support Layer — POM filament for Metal FFF

Ultrafuse TPU 64D — TPU filament for FFF. Tensile strength 37 MPa · Young's modulus 205 MPa · Elongation at break 399 %

Ultrafuse TPU 85A — TPU filament for FFF. Tensile strength 34 MPa · Young's modulus 20 MPa · Elongation at break 600 %

Ultrafuse TPU 95A — TPU filament for FFF. Tensile strength 44.2 MPa · Young's modulus 48.4 MPa · Elongation at break 661 %

Ultrasint PA11 — PA11 powder for SLS. Tensile strength 52 MPa · Young's modulus 1750 MPa · Elongation at break 28 %

Ultrasint PA11 Black — PA11 powder for SLS. Tensile strength 52 MPa · Young's modulus 1750 MPa · Elongation at break 26 %

Ultrasint PA11 Black CF — PA11 + Carbon Fiber powder for SLS. Tensile strength 82 MPa · Young's modulus 5900 MPa · Elongation at break 7 %

Ultrasint PA11 ESD — PA11 + Carbon Fiber powder for SLS. Tensile strength 65 MPa · Young's modulus 3150 MPa · Elongation at break 20 %

Ultrasint PA11 rCF — PA11 + Carbon Fiber powder for SLS. Tensile strength 84 MPa · Young's modulus 6000 MPa · Elongation at break 7.5 %

Ultrasint PP 1400 Black — PP powder for SLS. Tensile strength 29 MPa · Young's modulus 1250 MPa · Elongation at break 25 %

Ultrasint TPU 01 — TPU powder for MJF. Tensile strength 9 MPa · Young's modulus 85 MPa · Elongation at break 280 %

Ultrasint TPU 88A — TPU powder for SLS. Tensile strength 8 MPa · Young's modulus 75 MPa · Elongation at break 280 %

Ultrasint TPU 88A Black — TPU powder for SLS. Tensile strength 8 MPa · Young's modulus 85 MPa · Elongation at break 280 %

Ultrasint TPU 90A LT — TPU powder for SLS. Tensile strength 9 MPa · Young's modulus 110 MPa · Elongation at break 280 %